Aluminum Plate 5005 Quality Data Sheet/Characteristics/Chemistry composition:
| Si | Fe | Cu | Mn | Mg | Zn | Al |
| ≤0.30 | ≤0.70 | ≤0.20 | ≤0.20 | 0.5~1.1 | ≤0.20 | Remainder |
Aluminum Sheet 5005 H34 Mechanical Properties Standard：
| Tensile Strength (Mpa) | Elongation % | Density(g/cm3) |
| 100~205 | 1~8 | 2.85 |
Product Features:
The strength of the 5005 aluminum plate belt is equivalent to 3003, the meltingability, and good processing. The 5005 aluminum plate is similar to the 3003 alloy, which has medium strength and good corrosion resistance. The anode oxide film is brighter than the oxide film on the 3003 alloy, and coordinated with the color tone of 6063 alloy
Aluminum Sheet 5005 application:
Curtain wall, shipping building, auto inner plate, tank car, oil tank, storage tank, marine facilities etc.
How to Pack and ship the aluminum plate 5005?
Packing: Strong wooden pallet, with blue PVC films or paper-interleaved,
Max Gross weight skid 2500KGS;
For 1 x 20FCL can load 20 to 25 Tons max;
Surface: mill finish with blue PE films to protect the surface.
Product Features:
D5083 aluminum plate anodization is beautiful after treatment. The arc welding performance is good. The main alloy elements in the 5083 alloy are magnesium, which has good corrosion resistance and weldable performance, and medium intensity. Excellent corrosion resistance enables 5083 alloy to be widely used in maritime affairs such as ships, as well as cars, aircraft welding parts, and subway light rails. Drilling equipment, transportation equipment, missile parts, armor, etc. 25083 belongs to the AI-MG alloy, with a wide range of use, especially the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity. The main alloy element of 5083 is magnesium, which has good forming processing performance, corrosion resistance, weldability, and medium intensity. It is used to manufacture aircraft fuel tanks, oil pipes, transportation vehicles, ships, and ships, instrument, street lamp stands and rivets, rivets, rivets, rivets, rivets, and rivets, and rivets, and rivets, and rivets, and rivets, and rivets, and rivets, rivets, and rivets. Hardware products, electrical shells, etc. 3 AL-MG alloys are the most widely used rust-proof aluminum. This alloy has high strength, especially with anti-fatigue strength: high plasticity and corrosion resistance, not heat treatment and reinforcement. The plasticity is still good, the plasticity is low when it is cold, the corrosion resistance is good, the weldability is good, the cutting performance is poor, and it can be polished. Uses are mainly used to require high plasticity and good welding. Low load parts working in liquid or gas media, such as fuel tanks, gasoline or lubricants, various liquid containers, and other small load parts made of deep pull: The wire is used for rivets
Aluminum Plate 5083 Quality Data Sheet / Characteristics / Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Cr | Ti | Zn | Al |
| ≤0.4 | ≤0.40 | ≤0.10 | 0.4~1.0 | 4.0-4.9 | 0.05~0.25 | ≤0.15 | ≤0.25 | Remainder |
Product Usage:
5083 is commonly used in ships, ships, vehicle materials, vehicles and aircraft board welding parts, strict fire container, cold device, TV tower, drilling equipment, transportation equipment, missile components, armored, etc.
Product Features:
Aluminum -magnesium alloy and aluminum manganese alloy are collectively called rust -proof aluminum, because the alloy composition between the two has increased their anticorrosive performance.
The representative of aluminum manganese alloy is 3003, 3004, 3105, and aluminum and magnesium alloys according to the level of magnesium alloy content.
It is 5005 5252 5251 5050 5052 5754 5083 5056 5086 and so on. Typical use of 5086 aluminum plate: It is used to need high corrosion resistance, good weldability and medium -intensity occasions.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Cr | Ti | Zn | Al |
| ≤0.4 | ≤0.50 | ≤0.10 | 0.2~0.7 | 3.5-4.5 | 0.05~0.25 | ≤0.15 | ≤0.25 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Yield Strength(MPa) | Elongation(%) |
| ≥240 | ≥95 | ≥12 |
Product Usage:
It can be welded in
ships, cars and aircraft boards;
strict fire containers,
refrigeration devices,
TV towers,
installation equipment,
transportation equipment,
missile parts,
armored, etc.
Product Features:
The 5182 aluminum plate is AI-Mg rust-proof aluminum. The performance of 5182 aluminum plate is similar to 5A02, but because the amount of magnesium is slightly higher than 5A02, and a small amount of silicon is added, the welding properties are better than 5A02. The welding performance of tough, welding and welding is very good, and there are no differences between the two of other properties. 5182 belongs to the AI-M system alloy and has a wide range of use, especially the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity. The main alloy element of 5052 is magnesium, which has good forming processing performance, corrosion resistance, weldability, and medium intensity. It is used to manufacture aircraft fuel tanks, oil pipes, transportation vehicles, ships, and ships, instrument, street lamp stands and rivets, rivets, rivets, rivets, rivets, and rivets, and rivets, and rivets, and rivets, and rivets, and rivets, and rivets. Hardware product electrical shell, etc.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Cr | Ti | Zn | Al |
| ≤0.20 | ≤0.35 | ≤0.15 | 0.2~0.5 | 4.0~5.0 | ≤0.10 | ≤0.10 | ≤0.25 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Yield Strength(MPa) | Elongation(%) |
| ≥175 | ≥80 | ≥15 |
Product Usage:
5182 belongs to AI-MG-SI alloys and has a wide range of use. Especially the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity. The main alloy case of 5182 is magnesium, which has good forming processing performance, corrosion resistance, weldability, and medium intensity. It is used to manufacture aircraft fuel tanks, oil pipes, transportation vehicles and ships, meals, street lamp stands and rivets , Hardware products, electrical shells, etc. 2AL-MN alloys are the most widely used rust-proof aluminum. This alloy has high strength, especially with anti-fatigue strength: high plasticity and corrosion resistance, not heat treatment and reinforcement. It is still good. When it is cold, it has low plasticity, good corrosion resistance, good welding, poor cutting performance, and can be polished. Uses are mainly used to require high and good welding properties. Low load parts working in liquid or gas media, such as mailboxes, gasoline or lubricating pipes.
Product Features:
The main element of 5056 is magnesium. Magnesium can significantly improve the strength of aluminum but not reduce its plasticity. Aluminum -magnesium alloy has good resistance and welding performance.
5056 also contains a small amount of manganese and chromium. Adding manganese can improve the resistance of the alloy, especially the ability of anti -stress corrosion and cracking, and can ensure that the alloy has higher stability.
The role of chromium is similar to manganese, which can improve the ability of anti -stress corrodes, improve the body's metal and weld strength, and reduce the tendency of welding cracks.
Product Usage:
It is good in non -heat treatment of alloy, good cuttings, good cutting.
The surface is beautiful after the anode. Can be processed into optical mechanical components, ship components and wire clips. 5056 aluminum alloys are commonly used for rivets combined with riveting aluminum alloy and magnesium alloy.
There are also 5056 coated aluminum wires, which are widely used to make window screens and other wire products that require good corrosion resistance.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Al |
| ≤0.30 | ≤0.40 | ≤0.10 | 0.05~0.20 | 4.5~5.6 | 0.05~0.20 | ≤0.10 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Density(g/cm³) |
| ≤305 | 2.85 |
Product Features:
The 5A06 aluminum plate is AI-Mg rust-proof aluminum.
The 5A06 aluminum plate has high strength and corrosion stability.
The plasticity of the qi and welds of welded joints with fluorine arc welded in the annealing and squeezing state is acceptable.
The strength of gas welding and point welding its welding joint is 90 ~ 95%of the strength of the base; good cutting performance.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Zn | Al |
| ≤0.40 | ≤0.50 | ≤0.10 | 0.5~0.8 | 5.8~5.8 | ≤0.20 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Density(g/cm³) |
| ≤160 | 2.85 |
Product Usage:
1. It is a high -magnesium alloy, which has good strength in non -heat treatment alloys, good corrosion resistance, and good cuttings. The surface is beautiful after the anode. The arc welding performance is good. The main alloy elements in the 5A06 alloy are magnesium, which has good resistance and weldable performance, and medium intensity. Excellent corrosion resistance makes 5A06 alloy widely used in maritime affairs such as ships, as well as cars, aircraft welding parts, and subway light rails. , Drilling equipment, transportation equipment, missile parts, armor, etc.
2. 5A06 belongs to AI-MG alloys and has a wide range of use. Especially the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity. The main alloy of 5083 is magnesium, which has good forming processing performance, corrosion resistance, weldability, and medium intensity. It is used to manufacture aircraft fuel tanks, oil pipes, transportation vehicles and ships, meals, street lamp stands and riveting Booking, hardware products, electrical shells, etc.
3. AL-MN alloys are the most widely used rust-proof aluminum. This alloy has high strength, especially with anti-fatigue strength: high plasticity and corrosion resistance, not heat treatment and reinforcement. The plasticity is still good, the plasticity is low when it is cold, the corrosion resistance is good, the weldability is good, the cutting performance is poor, and it can be polished. Uses are mainly used to require high plasticity and good welding. Low load parts working in liquid or gas media, such as fuel tanks, gasoline or lubricants, various liquid containers, and other small load parts made of deep pull: Wiring for nails
Product introduction:
5052 belongs to the AI-MG alloy and has a wide range of use, especially the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity. The main alloy elements of 5052 are magnesium, which has good forming processing performance, corrosion resistance, weldability, and medium intensity. It is used to manufacture aircraft oil tanks, oil pipes, and gold parts of transportation vehicles and ships, instrument, street light brackets and rivets, rivets, rivets, rivets, rivets, rivets, and rivets, and rivets, and rivets, rivets, rivets, rivets, and rivets, and rivets, and rivets, rivets, and rivets. Hardware products, electric-device cases, etc.
Al-Mn is the most widely used rust-proof aluminum. This alloy is high, especially with anti-fatigue strength: high plasticity and corrosion resistance, not heat treatment and strengthening. When cold -handed hardening, the plasticity is low, the corrosion resistance is good, the weldability is good, the cutting performance is poor, and it can be polished. Uses are mainly used to require high plasticity and good welding. Low load parts working in liquid or gas media, such as fuel tanks, gasoline or lubricants, various liquid containers, and other small load parts made of deep pull: The wire is used for rivets.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Zn | Al |
| ≤0.25 | ≤0.40 | ≤0.10 | ≤0.10 | 2.2~2.8 | ≤0.10 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Yield Strength(MPa) | Density(g/cm³) |
| 173~244 | ≥70 | 2.85 |
Product process performance:
(1) Setting performance
(2) Welding performance
(3) Mechanical processing performance
Product Features:
5052 aluminum alloy is the most widely used rust -proof aluminum. This alloy is high, especially with anti -fatigue strength: high plasticity and corrosion resistance, not heat treatment and strengthening. During the hardening, the plasticity is low, the corrosion resistance is good, the weldability is good, the cutting performance is poor, and it can be polished.
Product Usage:
5052 is mainly used to require high plasticity and good welding properties. It is also commonly used for the rice and food of transportation vehicles and ships. Instrument, street light brackets and rivets, hardware products, electrical shells, etc. welding rod. Aerospace aluminum alloy material is a typical rust -proof alloy material.
Product Features:
5A05 is AI-MG rust-proof aluminum alloy, which cannot be strengthened. The magnesium content of the alloy is high, its strength is low, which is similar to 5A03 alloys. Cold deformation of alloy can increase the intensity, but decreases plasticity. The plasticity of the annealing state is high, and the plasticity of semi -cold is still hardened. The metal's corrosion resistance is good, and it is suitable for point welding, atomic hydrogen welding, gas welding, fluorine arc welding. Its cutting and processing is very poor when the annealing state, and the semi -cold state of hardening is still good.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Zn | Al |
| ≤0.50 | ≤0.50 | ≤0.10 | 0.3~0.6 | 4.8~5.5 | ≤0.20 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Yield Strength(MPa) | Elongation(%) |
| ≥225 | ≥110 | ≥15 |
Product Usage:
5A05 alloys are usually used to manufacture welded pipelines, welding fuel tanks and other liquid containers, and other parts, and other parts, wires, and rivets with high plastic plasticity, good corrosion resistance, and suffering from medium loads. Rivets need to perform anode oxidation treatment. In foreign countries, similar alloys (such as 5456) are used to make armor plates and high -strength structural parts. Storage tanks, pressure vessels, and marine supplies components.
Thermal treatment process:
1) Uniformly antidium: Heating 460 ~ 475 C; Insulation 12 ~ 14h; Air Cold
2) Quick annealing: Heating 310 ~ 350C; insulation time 30 ~ 120min: empty or water cooling
3) High temperature annealing: Heating 310 ~ 335C; when the thickness of the finished product is 6mm or <6mm, the insulation time is 30 ~ 180min or 30 ~ 120min: empty cold
4) Low temperature annealing: Heating 250 ~ 300C or 150 ~ 180C; the insulation time is 1 ~ 2H or 2 ~ 3H air cooling
Product Features:
The performance of 5A03 aluminum plate is similar to 5A02, but because the amount of magnesium is slightly higher than 5A02, a small amount of silicon is added, so the welding properties are better than 5A02. Very good, there are no big differences between the two of other properties. 5A03 belongs to the AI-MG alloy and has a wide range of use. In particular, the construction industry cannot be separated from this alloy. It is the most promising alloy. Good corrosion resistance, excellent welding, good cold processing, and medium intensity.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Zn | Al |
| 0.5~0.8 | ≤0.50 | ≤0.10 | 0.3~0.6 | 3.2~3.8 | ≤0.20 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Yield Strength(MPa) | Elongation(%) |
| ≥175 | ≥80 | ≥15 |
Product Usage:
5A03 AI-MG-alloy is the most widely used rust-proof aluminum. This alloy is high, especially with anti-fatigue intensity: high plasticity and corrosion resistance, not heat treatment and reinforcement. The time plasticity is still good, the plasticity is low when it is cold, the corrosion resistance is good, the weldability is good, the cutting performance is poor, and it can be polished. Uses are mainly used to require high plasticity and good welding. Low load parts working in liquid or gas media, such as mailboxes, gasoline or lubricants, various liquid containers, and other small load parts made of deep pull: The wire is used for rivets
Thermal treatment process:
1) Uniformly antidium: Heating 460 ~ 475C; Insulation 12 ~ 14h; Air Cold
2) Quick annealing: Heating 350 ~ 410 "C; insulation time 30 ~ 120min: empty or water cooling.
3) High temperature annealing: Heating 350 ~ 420C; when the thickness of the finished product is 26mm or <6mm, the thermal insulation time is 10 ~ 30 minutes or 2 ~ 10min: empty cold.
4) Low temperature annealing: heating 250 ~ 300C; the insulation time is 1 ~ 2h, empty cold
Product Features:
5A02 is AI-MG rust-proof aluminum alloy, which cannot be strengthened. The magnesium content of the alloy is low, its plasticity is high, the forming model, and the strength is low, but the strength of the 3A21 alloy is higher. Cold deformation can improve its strength and decrease in plasticity. The alloy is well -corrosive and is suitable for use in the marine environment. The welding of the alloy is good. Its cutting processing is poor, and the state of cherry blossoms can be improved.
Chemistry Composition:
| Si | Fe | Cu | Mn | Mg | Cr | Al |
| ≤0.40 | ≤0.40 | ≤0.10 | 0.15~0.40 | 2.0~2.8 | 0.15~0.40 | Remainder |
Mechanical performance:
| Tensile Strength(MPa) | Elongation(%) | Density(%) |
| ≥147 | ≥14 | ≥15 |
Product Usage:
5A02 alloys are suitable for welding structures and containers with high process plasticity and corrosion resistance, such as fuel tanks, gasoline and lubricating oil catheters, nails, flanges, and light loads, internal decorative parts of ships, vehicles, etc., etc. The wire is used as a rivet or a stripe.
Thermal treatment process:
1) Uniformly antidium: Heating 440 ° C; heat preservation 12 ~ 14h; empty cold.
2) Quick annealing: Heating 350 ~ 410C; insulation time 30 ~ 120 minutes; empty or water cooling.
3) High temperature annealing: Heating 350 ~ 420C; the thickness of the finished product of 26mm or <6mm is 210min or 10 ~ 30min: empty cold.
4) Low temperature annealing: heating 250 ~ 300C or 150 ~ 180C; the insulation time is 1 ~ 2h, empty cold
1050 belongs to 1 xxx series aluminum which is called pure aluminum sheet. It is made by virgin aluminum ingot, we can guarantee it is 99.5% purity, not made by aluminum scrap.
1050 Aluminum Sheet Chemistry Composition / A1050 Date Sheet:
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Al |
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | - | - | 0.05 | 0.03 | 99.5 |
1050 Aluminum Sheet Mechanical Properties / Properties of alloy 1050:
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | surface |
| 1050-O | 78Mpa (8Ksi -12Ksi) | 35 (above 2.5 Ksi) | Qualified | Qualified |
| 1050-H12 | 95Mpa (11Ksi - 16Ksi) | 18 (above 9 Ksi) | Qualified | Qualified |
| 1050-H14 / H24 | 123Map (12Ksi - 17Ksi) | 7 (above 9 Ksi) | Qualified | Qualified |
| 1050-H18 | 140 Map (above 16Ksi) | 4 (above 10Ksi) | Qualified | Qualified |
1050 H14 Aluminum Sheet coil application:
Since the pure aluminum sheet has good plasticity, conductivity, it is wildly used for cookware, lighting, lamps, road sign, auto part, trucks, PS boards, building decorations, Distribution cabinets, curtain walls, etc. The pure aluminum sheet is also called food grade aluminum, can be used for producing cookware and utensils.
Aluminum Sheet 1050 H14 Packing and Loading:
Surface with blue PE films or paper-interleaved.
Packing: Export wooden pallet packing suitable to prevent moisture and safe for ocean delivery.
Max package must not exceed 4500LBS, or as customer requirement.
For 1 x 20GP can load 25MT.
1060 Aluminum Sheet belongs to pure aluminum and the purity is 99.6% aluminum.
The same as other pure aluminum alloy numbers, 1060 aluminum sheet has good plasticity, conductivity, it is wildly used for cookware, lighting, lamps, road sign, auto part, truck body, PS board, Building Decoration, Distribution Cabinet, Curtain Wall, etc.
1060 Aluminum Sheet Properties/feature Standard:
ASTM-B209 ; GB/T3880-2012, EN485 Chemistry Composition
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Al |
| 1060 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | - | - | 0.05 | 0.03 | 99.6 |
1060 Aluminum Sheet mainly Mill finish, with blue PE films or paper-interleaved.
This alloy can’t make the heat treatment and the main temper are H24, H14, also can be produced with fully annealed and be soft temper. 1060 aluminum sheet can also be wildly used for producing aluminum circles and discs which is very soft and good for spinning and deep drawing.
1060 H24 Aluminum Sheet coil application:
Since the pure aluminum sheet has good plasticity, conductivity, it is wildly used for cookware, lighting, lamps, road sign, auto part, truck bodies, PS boards, building decorations, Distribution cabinets, Curtain walls, etc. The pure aluminum sheet is also called food-grade aluminum, can be used for producing kitchen utensils.
1100 Aluminum Sheet Introduction
The alloy 1100 is one of the alloy numbers with the most aluminum content among all series. The purity of 1100 can reach more than 99.00%. Since it does not contain other metal elements, it is a single production process and relatively inexpensive. This makes it be the most commonly used series in the normal industry. It has conductive, good thermal conductivity, which is very good and only after silver, copper, and gold. Low density: The density of pure aluminum is 2.71KG/M3. about 35% of iron.
1100 Aluminum Sheet Chemistry Composition & Mechanical Properties & Features:
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Al |
| 1100 | 0.95 | 0.05-0.2 | 0.05 | - | - | - | 0.1 | - | 99 | |
Aluminum Sheet 1100 H14 Application and Usage:
Chemical equipment,
conductive materials,
chemical equipment,
instruments,
highway road signs,
motor vehicle license plates,
cookware,
building decoration materials,
hardware and cooking utensils,
machine part;
1100 H24 Aluminum Sheet Packing and Loading:
Seaworthy packages to be protected from humidity.
Package to Avoid All Moisture Contamination
Heat#’s must be recorded on all bundles
Do not mix heats within bundles
Bundle individual sizes separately
2-3 mils medium tack clear or clear blue PVC films on one side.
Critical surface quality: No chatter, no rolling marks, no weld, no stains accepted;
3003 H14 Aluminum Sheet Features:
① 3003 aluminum alloy with Mn as the main alloying element, which cannot be reinforced by heat treatment.
② good plasticity, good welding performance. But corrosion resistance is slightly stronger than alloy 1050. It belongs to a medium-strength aluminum alloy.
③There are two ways of annealing temperature. One is low-temperature annealing which requires only a temperature of 260-360℃, another is high-temperature annealing which requires at least 370-490℃.
We only use 99.7% pure aluminum to manufacture aluminum sheets, aluminum coil, aluminum roofing, aluminum disc, and more. On average, we can produce over 1,000 Tons of aluminum products while maintaining their quality.
Aluminum Sheet Plate 3003 Chemistry Composition & Mechanical Properties & Features:
| Alloy | Si | Fe | Cu | Mn | Mg | Zn | Al |
| 3003 | 0.6 | 0.7 | 0.05~0.20 | 1.0~ 1.5 | --- | 0.1 | remainder |
| Alloy | Tensile strength | Stretch rate（%） | Dimension Control | Surface |
| Aluminum sheet 3003-H14 | Standard Value >195 | Standard Value ≥1 | Qualified | Qualified |
Application and Usage:
It is mainly used for working with slightly higher strength than Series 1, such as pressure tank, storage tank, heat preservation material, mechanical parts, automobile, aircraft fuel tank, etc. It is used in air conditioners, refrigerators, cars, planes. Conventional applications in air conditioning, refrigerators, under the car, and other humid environments. The price is higher than 1x x x x series and it is a more commonly used alloy series.
3004 Aluminum Sheet belongs to the Anti-Rust series. The content of magnesium alloy can almost reach 1%, it is a product with good anti-rust performance. Huachuang Aluminum Industry company’s 3004 aluminum sheets are produced by Hot-Rolling process. The minimum order quantity is 5 tons. Although this series of aluminum plate is divided into aluminum-manganese alloy(3000 series aluminum), the higher magnesium alloy is more like aluminum-magnesium (5000 series aluminum) alloy products, the material’s high quality anti-rust, corrosion resistance determines a wide range of use and long service life.
Aluminum Sheet 3004 Packing and Loading:
The aluminum plate is Seaworthy packages to be protected from humidity, Avoid All Moisture Contamination. Heat#’s recorded on all bundles, Do not mix heats within bundles, Bundle individual sizes separately. We will put 2-3 mils medium tack clear or clear blue PVC one side.
Critical surface quality: No chatter, no Pitt marks, no weld, no stains accepted; Skids suitable to load in Flat-Rack contains.
Aluminum plate is the thickness of more than 0.2mm to 500mm below,200mm width, length within 16m of the aluminum material is called aluminum sheet or aluminum sheet,0.2mm below for aluminum,200mm width for platoon or strip (of course, with the progress of large equipment, the widest can do 600mm aluminum plate is also more).
Aluminum plate refers to the rectangular plate processed by aluminum ingot rolling, which is divided into pure aluminum plate, alloy aluminum plate, thin aluminum plate, medium thickness aluminum plate, pattern aluminum plate.
| Thickness | 0.1-400mm，etc | Length: | 100-12000mm，or as required |
| Width | 20-3000mm，etc | Standard: | ASTM，AISI，JIS，GB， DIN，EN |
| Certification: | ISO, SGS，BV | ||
| Surface finish | mill,bright,polished,hair line,brush,sand Blast,checkered,embossed,etching,etc | ||
| Grade | 1000 Series: 1050 1060 1070 1100 1200 1235 etc. | ||
| 3000 Series: 3003 3004 3005 3104 3105 3A21 etc. | |||
| 5000 Series: 5005 5052 5083 5086 5154 5182 5251 5754 etc. | |||
| 6000 Series: 6061 6063 6082 6A02 etc. | |||
| 7000 Series: 7050 7475 7075 etc. | |||
| Temper | H12,H14,H16,H18,H20,H22,H24,H26,H28,H32,H36,H38,HO,H111,H112,H114,H116,H118,H321. | ||
| Payment Terms | T/T, L/C at sight,West Union,D/P,D/A,Paypal | Loading port | any port in China |
| Packing | standard export packing (inside:water proof paper,outside:steel covered with strips and pallets) | ||
| Container size | 20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) | ||
| 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) | |||
| 40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High) | |||
Aluminum plate is usually divided into the following two kinds:
1. According to the composition of alloy:
High purity aluminum plate (rolled from high purity aluminum content above 99.9)
Pure aluminum plate (basically rolled from pure aluminum)
Alloy aluminum plate (composed of aluminum and auxiliary alloys, usually aluminum copper, aluminum manganese, aluminum silicon, aluminum magnesium, etc.)
Composite aluminum plate or brazed aluminum plate (special purpose aluminum plate material obtained by means of composite of multiple materials)
Aluminum-clad aluminum plate (aluminum plate coated with thin aluminum plate for special use)
2. According to thickness :(unit mm)
Sheet (aluminum sheet) 0.15-2.0
Conventional sheet (aluminum sheet) 2.0-6.0
Medium plate (aluminum plate) 6.0-25.0
Aluminum plate 25-200
Five aluminum panels with rib pattern
Five aluminum panels with rib pattern
Super thick plate more than 200
use
1. Lighting lighting
2, solar reflector
3, architectural appearance
4, interior decoration: ceiling, wall, etc.
5, furniture, cabinets
6, the elevator
7. Signs, nameplates, cases and bags
8, car interior and exterior decoration
9. Interior decorations: such as photo frames
10, household appliances: refrigerator, microwave oven, audio equipment, etc.
11. Aerospace and military aspects, such as China's large aircraft manufacturing, Shenzhou spacecraft series, satellites and other aspects. 12, mechanical parts processing 13, mold manufacturing 14, chemical/insulation pipeline coating. 15. High quality board