Properties of 201 stainless steel sheet:
201 stainless steel grade: 1Cr17Mn6Ni5N
201 stainless steel has certain acid and alkali resistance, high density, no bubbles, no pinholes, etc. It is used to produce high-quality materials for various watch cases and watchband back covers. Mainly used to make decorative tubes, industrial tubes, and some shallow stretched products.
| Width | 1000mm-2000mm or as customized |
| Thickness | Cold rolled:0.3mm-3.0mmHot rolled:3.0mm-100mm |
| Length | 1000mm-6000mm or as requested |
| Surface | No.1,2b,8k,2d,Ba,No.4,No.6,No.8, etc. |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.15 | ≤0.75 | 5.5~7.5 | 16.0~18.0 | 3.5~5.5 | ≤0.03 | ≤0.060 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Hardness |
| ≥635 | ≥440 | 7.93 | ≥40 | Annealing,≤223HBQuenching and tempering,≥192HB |
202 Stainless Steel Sheet :
202 stainless steel is one of the 200 series stainless steel, the national standard model is 1Cr18Mn8Ni5N.
202 stainless steel is widely used in building decoration, municipal engineering, highway guardrail, hotel facilities, shopping malls, glass handrails, public facilities and other places.
Chemical Comppsition :
Properties of 304 stainless steel sheet:
304 stainless steel grade: 0Cr18Ni9 (0Cr19Ni9) 06Cr19Ni9 S30408
304 has a wide range of uses, with good corrosion resistance, heat resistance, low temperature strength and mechanical properties; it has good hot workability such as stamping and bending, and no heat treatment hardening phenomenon (non-magnetic, use temperature -196°C~800°C). 304 stainless steel has excellent corrosion resistance and good resistance to intergranular corrosion.
| Name | 304 stainless steel sheet |
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | 0.1-200mm |
| Surface | 2B,NO.1,NO.4,HL,BA,BK |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.08 | ≤1.0 | ≤2.0 | 18.0~20.0 | 8.0~10.5 | ≤0.03 | ≤0.035 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Melting point(°C) | ||
| ≥520 | ≥170 | 7.93 | ≥40 | 1398~1420 | ||
304L stainless steel, also known as ultra-low carbon stainless steel, is a kind of universal stainless steel material, widely used in the production of equipment and parts requiring good comprehensive properties (corrosion resistance and formability).
Composition Content:
| Grade | Euronorm | China GB | Japanese JIS | |
| No. | ||||
| 304L | 1.4307 | 00Cr19Ni10 | SUS304L | |
Chemical Comppsition :
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304L | Min. Max. | ≤0.03 | ≤2.0 | ≤1.00 | ≤0.045 | ≤0.03 | 18.0～20.0 | / | 9.0～12.0 | |
Standard Specification：
| Thickness | 0.3-3.0mm; 3-6mm |
| Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
| Surface | 2B, 2D, BA, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc |
| Finish | Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered sheet, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
309S is a free cutting stainless steel with sulfur, used in applications where free cutting and high surface smoothness are the main requirements.
309S corresponding to the Chinese brand is 0Cr23Ni13, the American standard S30908 (AISI, ASTM) characteristics and use: corrosion resistance, heat resistance are better than 0Cr19Ni9.
The 309S is a variant of the lower carbon 309 stainless steel for use where soldering is required.
Properties of 310S stainless steel sheet:
310s stainless steel grade: Old grade 0Cr25Ni20/new grade 06Cr25Ni20
310S stainless steel is an austenitic chromium-nickel stainless steel that has good oxidation resistance, corrosion resistance, and high temperature resistance. Because of the higher percentage of chromium and nickel, it has much better creep strength and can continue to operate at high temperatures. Has good high temperature resistance.
| Width | 1000mm-2000mm or as customized |
| Thickness | Cold rolled 0.3-3.0mm hot rolled 3.0-100mm |
| Length | 1000mm - 6000mm or as customer's request |
| Surface | No.1,2b,8k,2d,Ba,No.4,No.6,No.8, etc. |
| Standards | AISI,ASTM,JIS,SUS,GB |
| Samples | Available |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.08 | ≤1.50 | ≤2.0 | 24.0~26.0 | 19.0~22.0 | ≤0.08 | ≤0.030 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Melting point(°C) | ||
| ≥520 | ≥205 | 7.93 | ≥50 | 1398~1454 | ||
316 Stainless steel sheet Price in China ,Manufacturer of 316 Stainless Steel sheet
316 stainless steel because of the addition of Mo element, so that its corrosion resistance, and high temperature strength has been greatly improved, high temperature resistance can reach 1200-1300 degrees, can be used under harsh conditions.
Application: Seawater equipment, chemical, dye, paper making, oxalic acid, fertilizer and other production equipment;
Photographs, food industry, coastal facilities, ropes, CD rods, bolts, nuts.
Equivalent Material：
| Grade | Euronorm | China GB | Japanese JIS | |
| No. | ||||
| 316 | 1.4401 | 0Cr17Ni12Mo2 | SUS316 | |
Chemical Comppsition :
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 | Min. Max. | ≤0.08 | ≤2.00 | ≤1.00 | ≤0.035 | ≤0.03 | 16.0-18.5 | 2.0-3.0 | 10.0-14.0 | |
Properties of 316L stainless steel coil:
Grade 316L Stainless Steel Coil is standard molybdenum austenitic stainless steel have lower carbon percentage. Addition of molybdenum gives better corrosion resistant properties and lower carbon percentage offers high weldability & formability. However, there is no appreciable price difference between 316 and 316L Stainless Steel.
| Thickness | 0.2mm-5.0mm |
| Width | 3.2mm-1500mm |
| Length | 2000mm,2440mm,3000mm,5800mm,6000mm or as customized |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | ||||||
| 316L | Min | – | – | – | – | – | 16 | 2 | 10 | – | |||||
| Max | 0.03 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | ||||||
Mechanical properties:
| Grade | Tensile Str(MPa) min | Yield Str0.2% Proof(MPa) min | Elong(% in 50mm) min | Hardness | |||||||||||
| Rockwell B (HR B) max | Brinell (HB) max | ||||||||||||||
| 316L | 485 | 170 | 40 | 95 | 217 | ||||||||||
Properties of 321 stainless steel sheet:
321 stainless steel grade: 1Cr18Ni9Ti
321 stainless steel is a material with excellent high temperature stress rupture (Stress Rupture) performance and high temperature creep resistance (Creep Resistance) stress mechanical properties are better than 304 stainless steel.
| Treatment | Hot rolled and Cold rolled |
| Surface | No.1 / 2B / No.4 / HL / Brushed / BA / 8K Mirror / Embossed / Etched etc |
| Thickness Range | 0.3 - 3mm ( Cold Rolled Process ) 3 - 100mm or more (Hot Rolled Process) |
| Standard | ASTM, AISI, SUS, JIS, EN, DIN, GB, ASME, etc. |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.08 | ≤1.0 | ≤2.0 | 17.0~19.0 | 9.0~12.0 | ≤0.03 | ≤0.045 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Melting point(°C) | ||
| ≥520 | ≥205 | 7.93 | ≥40 | 1398~1427 | ||
The 409L stainless steel has strong resistance to corrosion, high temperature and fatigue, and can realize the life and lightweight of exhaust system components.
409L Stainless steel sheet Price in China ,Manufacturer of 409L Stainless Steel sheet
Equivalent Material：
| Grade | Euronorm | Japanese JIS | ISO | |
| No. | ||||
| 409L | 1.4512 | SUH409L | X2CrTi12 | |
Chemical Comppsition :
(1) When 409L steel crystallizes, the solid-liquid two-phase zone is very small, less than 30℃;
(2) There is almost no γ phase at high temperature.
The carbon content of 409L steel is very low, even if δ phase is present, the amount is very small.
Therefore, there is no significant impact on performance.
409L steel from high temperature to low temperature almost no α→γ phase transformation, so the grain is easy to grow up, there are thick ferrite structure, low strength, in continuous casting, after the slab is cut up, prone to bend phenomenon, affect the normal production.
The main problem during crystallization of 409L steel is the degradation of properties caused by coarse grain size≥192HB
Properties of 410 stainless steel sheet:
410 stainless steel grade:1Cr13
Has good corrosion resistance, machinability, general purpose blades, valves. High strength; excellent machinability; hardened after heat treatment; magnetic; not suitable for harsh corrosive environments.
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | 0.1-100mm thickness |
| Width | 10-2500mm |
| Dimensions | Cold rolled 0.5-6.4mmHot rolled 3.0-10.0mm |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.15 | ≤1.00 | ≤1.00 | 11.5~13.5 | 8.0~10.5 | ≤0.03 | ≤0.04 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Melting point(°C) | ||
| ≥440 | ≥205 | 7.7 | ≥20 | 460 | ||
Properties of 430 stainless steel coil:
Stainless Steel 430 Coils are non-hardened steel contain 17% chromium & 0.75% nickel and belong to ferrite group of steels. These stainless steel coils are famous for their outstanding corrosion resistance and good formability. As UNS S43000 SS Coils possess some top quality features, coils are broadly used in chemical applications.
| Thickness | 0.2mm-5.0mm |
| Width | 3.2mm-1500mm |
| Length | 2000mm,2440mm,3000mm,5800mm,6000mm or as customized |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| Grade | C | Mn | Si | P | S | Cr | Ni | Mo | |
| 430 | Min | – | – | – | – | – | 16 | – | – |
| max | 0.12 | 1 | 1 | 0.04 | 0.03 | 18 | 0.75 | – |
Mechanical properties:
| Grades | SS 430 |
| Tensile Strength (MPa) min | 450 |
| Yield Strength 0.2% Proof (MPa) min | 205 |
| Elongation (% in 50mm) min | 22 |
| Hardness Rockwell B (HR B) max | 89 |
| Hardness Brinell (HB) max | 183 |
SUS444 (00Cr18Mo2) is a ferritic stainless steel with ultra-low carbon and nitrogen content, 18% chromium and 2% molybdenum, and high corrosion resistance.The yield strength of 444 is equivalent to 1.5 times of carbon steel and 6 times of fiberglass steel. It has outstanding advantages in shock resistance, snow resistance, wind pressure resistance and impact resistance.
SUS444 ferritic stainless steel has high thermal conductivity, about 130% ~ 150% of Cr-Ni austenitic stainless steel, which is very suitable for heat exchange purposes.
Equivalent Material：
| Grade | Euronorm | China GB | Japanese JIS | |
| No. | ||||
| 444 | 1.4521N | 00Cr18Mo2 | SUS444 | |
Chemical Comppsition :
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 444 | Min. Max. | ≤0.025 | ≤1.00 | ≤1.00 | ≤0.04 | ≤0.03 | 17.5~19.5 | 1.75~2.5 | ≤1.00 | ≤0.035 |
Properties of 904L stainless steel sheet:
904L super austenitic stainless steel is a low-carbon, high-nickel, molybdenum austenitic stainless and acid-resistant steel, which is a proprietary material imported from France H·S. It has good activation-passivation transformation ability, excellent corrosion resistance, good corrosion resistance in non-oxidizing acids such as sulfuric acid, acetic acid, formic acid, and phosphoric acid, and good corrosion resistance in neutral chloride-containing media It has good pitting corrosion resistance and good resistance to crevice corrosion and stress corrosion. It is suitable for sulfuric acid of various concentrations below 70°C, and has good corrosion resistance in acetic acid at any concentration and at any temperature and the mixed acid of formic acid and acetic acid under normal pressure.
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | Customized |
| Denmension | Requested |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.02 | ≤1.0 | ≤2.0 | 19.0~23.0 | 8.0~10.5 | ≤0.03 | ≤0.045 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Melting point(°C) | ||
| ≥490 | ≥216 | 8.24 | ≥35 | 1300~1390 | ||
Properties of 2205 stainless steel sheet:
Duplex stainless steel 2205 standard number: ASTM A240/A240M--01 duplex stainless steel 2205 alloy is a duplex stainless steel composed of 22% chromium, 2.5% molybdenum and 4.5% nickel-nitrogen alloy. It has high strength, good impact toughness and good overall and local stress corrosion resistance.
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | Customized |
| Denmension | Requested |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.03 | ≤1.0 | ≤2.0 | 21.0~24.0 | 4.5~6.5 | ≤0.03 | ≤0.04 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | HV | ||
| ≥620 | ≥450 | 7.8 | ≥25 | ≥18 | ||
Properties of 440C stainless steel sheet:
440C steel is a martensitic stainless steel. The carbon content is 1.0%, and the chromium content is 16-18%. It has strong rust resistance and is a high-quality stainless steel.
Scope of application: Mainly used to manufacture bearing parts that work in corrosive environments and non-lubricated strong oxidizing atmospheres. 440C has good high-temperature dimensional stability, so it can also be used as corrosion-resistant high-temperature bearing steel. In addition, it can also be used to manufacture high-quality knives, such as medical scalpels, scissors, nozzles, bearings, etc. 440C has a lower ability to withstand dynamic loads.
| Name | 440C stainless steel sheet |
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | Customized |
| Denmension | Requested |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| 0.95~1.20 | ≤1.0 | ≤1.0 | 16.0~18.0 | ≤0.60 | ≤0.03 | ≤0.035 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Hardness | Pre-heat temperature (°C) | ||
| ≥560 | ≥250 | 7.85 | Annealing,≤269HB | 649~816 | ||
Properties of 420 stainless steel sheet:
420 stainless steel grade:2Cr13
420 stainless steel is a martensitic stainless steel with certain wear resistance and corrosion resistance, and high hardness. It is suitable for all kinds of precision machinery, bearings, electrical, equipment, instruments, meters, transportation tools, household appliances, etc. It is mostly used to manufacture parts that are resistant to atmospheric, water vapor, water and oxidizing acid corrosion.
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | Customized |
| Denmension | Requested |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| 0.16~0.25 | ≤1.0 | ≤1.0 | 12.0~14.0 | ≤0.75 | ≤0.03 | ≤0.04 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Impact energy Akv(J) | ||
| ≥625 | ≥440 | 7.7 | ≥20 | ≥63 | ||
Properties of 2507 stainless steel sheet:
2507 is a ferritic-austenitic (duplex) stainless steel, which combines the most beneficial properties of many ferritic steels and austenitic steels. Due to the high content of chromium and molybdenum, the steel has extremely high chromium and molybdenum content. Good resistance to pitting corrosion, crevice corrosion and uniform corrosion. The dual-phase microstructure ensures that the steel has a high resistance to stress corrosion cracking, and the mechanical strength is also high.
| Standard | GB,AISI,ASTM,ASME,EN,BS,DIN,JIS |
| Thickness | Customized |
| Denmension | Requested |
| Samples | Available |
| Packing | Standard or as your requirement |
Chemical composition:
| C | Si | Mn | Cr | Ni | S | P |
| ≤0.03 | ≤0.8 | ≤1.2 | 24.0~26.0 | 6.0~8.0 | ≤0.02 | ≤0.035 |
Mechanical properties:
| Tensile strength σb (MPa) | Conditions yield strength 0.2 sigma (MPa) | Density(g/cm) | Elongation(A/%) | Hardness | ||
| ≥793 | ≥550 | 7.8 | ≥15 | ≤29 | ||